Modèl Pa gen.: HONYFR4-Washer
Brand: Onony
Vann Inite | : | Piece/Pieces |
Kalite pake | : | Ekspòtasyon katon |
Customized FR4/G10 izolasyon gasket MICARTA FR4 G10 epoksidik fib vè se fèy epoksidik, ke yo rele tou izolasyon fim, fèy vèr, ak fèy epoksidik, li se te fè nan alkali-gratis twal vè enpreye ak epoksid pa pwosesis anba chalè ak presyon. Li posede karaktè rezistans a tanperati ki wo, entansite segondè, klas rezistan flanm dife, UL94-V0, segondè pwopriyete mekanik ak pwopriyete dielèktrik, bon rezistans chalè, bon Harmony, elatriye.
Kalite pwodwi: èpoksi Fiberglass Plastifye fim
Materyèl: flanm dife rezistan epoksidik + vè fib twal
Karakteristik prensipal
1) flanm dife.
2) segondè rezistans vòltaj.
3) rezistans imidite.
4) rezistans chalè.
5) Rezistans Tanperati: 150-180
6) Bon etablisman, sifas ki lis, pa gen okenn twou.
Aplikasyon
Nan mekanik, elektrik ak elektwonik segondè estrikti izolasyon segondè
Itilize nan kondisyon izolasyon elektrik.
Pati machin chimik
Jeneral machin pati ak Kovèti pou, dèlko, kousinen, baz, defle
Dèlko, transfòmatè, lanp, varyateur, motè.
Item
|
Value
|
||
Specific gravity
|
G/cm & sup3;
|
1,70 ~ 1,90
|
|
° C
|
155
|
||
Bending strength min
|
Longitudinal
|
MPA 343,2
|
|
Cross
|
MPA 284,4
|
||
Tensile strength min
|
Longitudinal
|
MPA 294,2
|
|
Cross
|
KJ/sqm 147,1
KJ/sqm 98,1 |
||
Impact resistance min
|
Cross
Longitudinal |
KJ/sqm 147,1
KJ/sqm 98,1 |
|
Surface resistance min
|
Under normal condition
After immersion in water |
Ohm
|
Ω 1x1013
Ω 1x1011 |
Volume resistance min
|
Under normal condition
After immersion in water |
Ohm cm
|
Ω cm 1x1013
Ω cm 1x1011 |
Insulation Resistance parallel
To laminate ionmin |
Under normal condition
After immersion in water |
Ohm
|
Ω 1x1010
Ω 1x108 |
Dielectric loss Max
|
50Hz
|
KV/mm 0,05
|
|
Impact strength
Perpendicular to sheets (At 90 ± 2 ° C in transformer oil) Min |
Thick 0,5 ~ 1mm
|
KV/mm 22,0
|
|
Thick 0,5 ~ 1mm
|
KV/mm 20,0
|
||
Thick 0,5 ~ 1mm
|
KV/mm 18,0
|
||
Leaf with thick more than 3mm will be edited up to 3mm from one side
|
KV/mm 18,0
|
||
Breakdown voltage parallel to sheets
(At 90 ± 2 ° C in transformer oil) |
Min
|
KV
|
30,0
|
FR-4 fib vè plastik laminated plak izolan, plastik fib vè
1) FR-4 twal vè epoksidik te plak la pwodwi laminated, materyèl yo espesyal elektwonik tankou twal tranpe nan epoksidik fenol résine pa tanperati ki wo & #12289; Segondè presyon ak cho peze.
2) Klas tèmik: Klas B.
3) Epesè: 0,2-50mm
4) Gwosè: lajè/longè (mm) 1020*2040mm, 1020*1200mm
5) Koulè: vèt/nwa
Deklarasyon sou vi prive: Konfidansyalite ou trè enpòtan pou nou. Konpayi nou an pwomèt pou nou pa divilge enfòmasyon pèsonèl ou nan nenpòt ki EXPANY ak soti otorizasyon eksplisit ou.
Ranpli plis enfòmasyon pou ki ka jwenn an kontak ak ou pi vit
Deklarasyon sou vi prive: Konfidansyalite ou trè enpòtan pou nou. Konpayi nou an pwomèt pou nou pa divilge enfòmasyon pèsonèl ou nan nenpòt ki EXPANY ak soti otorizasyon eksplisit ou.